| temperature resistant, moisture resistant, for bonding of wood, synthetic materials, e.g. polyamide, PVC, PMMA, polystyrene and several elastomeres, e.g. rubber, EPDM, viton among each other and with metals and ceramics | |
| Strength class: | high strength |
| Curing system: | humidity |
| Viscosity: | 3000 |
| Chemical type: | ethyl-cyanoacrylate |
| Final Strength: | 20 hours |
| Fixture Time: | 10 - 15 seconds |
| Appearance: |  |
BEST-CA 233T is a one-component, solvent free cyanoacrylate adhesive based on ethyl-cyanoacrylate.
BEST-CA 233T is specially designed for temperature- and humidity-resistant bonding of wood and plastics, e.g. polyamide, PVC, PMMA, polystyrene and various elastomeres, e.g. rubber, EPDM and viton amongst each other and with metals and ceramics.
BEST-CA 233T is very fast cure. After full cure the adhesive is high strength and temperature resistant.
BEST-CA 233T is ready-to-use and can be applied from the original container.
BEST-CA 233T is applied spot-wise or bead like. Assemble parts by using short, firm pressure. Curing process starts within seconds. On most materials fixture time is reached within 10 to 15 seconds. 85 % of final cure is reached after 30 minutes, 100% after 20 hours. The rate of cure depends on the ambient relative humidity. A relative humidity of 40 to 60% will lead to best results. Lower values may delay cure.
Bonding surfaces must be dry, free of dust and grease as well as other contaminants. Sand-blasting, grinding and staining bonding surfaces will enhance adhesion on bonding surfaces.
CHEMICAL AND ENVIRONMENTAL RESISTANCE
BEST-CA adhesives show good resistance to changing climatic conditions and chemical influences.
product inquiry for a sample to CA 233T
Only for commercial customers and for serial production.
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.