Article
Group / Description
Curing Method
Chemical type
Final strength
Fixture time
Article:
 PU 1517
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, aluminum, steel, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
50 000
Chem. Basis:
polyurethane
Endfestigkeit:
24 hours
Handfestigkeit:
60 - 180 minutes
Article:
 PU-1504
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, aluminum, steel, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
50 000
Chem. Basis:
polyurethane
Endfestigkeit:
4 hours
Handfestigkeit:
1 - 5 minutes
Article:
 PU-1505
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, aluminum, steel, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
50 000
Chem. Basis:
polyurethane
Endfestigkeit:
8 hours
Handfestigkeit:
5 - 15 minutes
Article:
 PU-1507
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, aluminum, steel, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
60 000
Chem. Basis:
polyurethane
Endfestigkeit:
8 hours
Handfestigkeit:
5 - 15 minutes
Article:
 PU-1512
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, aluminum, steel, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
50 000
Chem. Basis:
polyurethane
Endfestigkeit:
3 hours
Handfestigkeit:
45 seconds to 3 minutes
Article:
 PU-1513
Group / Description
two-component polyurethane adhesive

Für das Strukturkleben von Thermoplasten, Wärmehärtenden Kunststoffen, Aluminium, Stahl, Zement, Holz, Glas.
AM:
polyaddition

Viscosity/mPa⋅s:
50.000 mPa s
Chem. Basis:
Polyurethan
Endfestigkeit:
4 Stunden
Handfestigkeit:
5 Minuten
Article:
 PU-1516
Group / Description
two-component polyurethane adhesive

for structural bonding of thermoplastics, thermosetting synthetic materials, steel, aluminum, cement, wood, glass.
AM:
polyaddition

Viscosity/mPa⋅s:
50 000
Chem. Basis:
polyurethane
Endfestigkeit:
12 hours
Handfestigkeit:
20 - 60 minutes