BEST-MK anaerobic adhesives
Article
Group / Description
Curing Method
Chemical type
Final strength
Fixture time
Group / Description
thread locker , low strength
for securing and sealing of screw and threaded connections
AM: thread locker , low strength
for securing and sealing of screw and threaded connections
anaerobic
Viscosity/mPa⋅s:
200
Chem. Basis: Viscosity/mPa⋅s:
200
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
thread locker , low strength
for securing of screws, sealing of threaded and pipe connections
AM: thread locker , low strength
for securing of screws, sealing of threaded and pipe connections
anaerobic
Viscosity/mPa⋅s:
1000 thix
Chem. Basis: Viscosity/mPa⋅s:
1000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 25 minutes
Group / Description
thread locker , medium strength
for securing and sealing of screw and threaded connections
AM: thread locker , medium strength
for securing and sealing of screw and threaded connections
anaerobic
Viscosity/mPa⋅s:
200
Chem. Basis: Viscosity/mPa⋅s:
200
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , medium strength
for securing and sealing of screw and threaded connections
AM: thread locker , medium strength
for securing and sealing of screw and threaded connections
anaerobic
Viscosity/mPa⋅s:
600 thix
Chem. Basis: Viscosity/mPa⋅s:
600 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , medium strength
securing of screws, sealing of threaded and screw connections
AM: thread locker , medium strength
securing of screws, sealing of threaded and screw connections
anaerobic
Viscosity/mPa⋅s:
1000 thix
Chem. Basis: Viscosity/mPa⋅s:
1000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , medium strength
AM: thread locker , medium strength
anaerobic
Viscosity/mPa⋅s:
1.000 thix
Chem. Basis: Viscosity/mPa⋅s:
1.000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 20 minutes
Group / Description
thread locker , medium strength
for securing and sealing of passive and inactive surfaces without the use of an activator
AM: thread locker , medium strength
for securing and sealing of passive and inactive surfaces without the use of an activator
anaerobic
Viscosity/mPa⋅s:
1.000 thix
Chem. Basis: Viscosity/mPa⋅s:
1.000 thix
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 6 minutes
Group / Description
thread locker , high strength
hard to disassemble, very low viscous, good capillary action, also suitable for subsequent application and waterproofing of grey cast iron
AM: thread locker , high strength
hard to disassemble, very low viscous, good capillary action, also suitable for subsequent application and waterproofing of grey cast iron
anaerobic
Viscosity/mPa⋅s:
12
Chem. Basis: Viscosity/mPa⋅s:
12
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , high strength
high strength, low viscous thread locking and sealing
AM: thread locker , high strength
high strength, low viscous thread locking and sealing
anaerobic
Viscosity/mPa⋅s:
500
Chem. Basis: Viscosity/mPa⋅s:
500
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , high strength
for securing and sealing of inactive and passive surfaces without the use of an activator
AM: thread locker , high strength
for securing and sealing of inactive and passive surfaces without the use of an activator
anaerobic
Viscosity/mPa⋅s:
500
Chem. Basis: Viscosity/mPa⋅s:
500
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 6 minutes
Group / Description
thread locker , high strength
thread locking and sealing, hard to disassemble
AM: thread locker , high strength
thread locking and sealing, hard to disassemble
anaerobic
Viscosity/mPa⋅s:
1000 thix
Chem. Basis: Viscosity/mPa⋅s:
1000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
thread locker , high strength
thread locker, low viscous, hard to disassemble, for bonding of adherend, temperature resistant up to 220°C (long term exposure)
AM: thread locker , high strength
thread locker, low viscous, hard to disassemble, for bonding of adherend, temperature resistant up to 220°C (long term exposure)
anaerobic
Viscosity/mPa⋅s:
300
Chem. Basis: Viscosity/mPa⋅s:
300
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
thread locker , high strength
medium viscous threadlocker for all thread sizes, hard to disassemble, temperature resistant up to 220°C (constant exposure)
AM: thread locker , high strength
medium viscous threadlocker for all thread sizes, hard to disassemble, temperature resistant up to 220°C (constant exposure)
anaerobic
Viscosity/mPa⋅s:
1000 thix
Chem. Basis: Viscosity/mPa⋅s:
1000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
anaerobic/UV-lightcuring , high strength
low viscous, capillary, for subsequent bonding
AM: anaerobic/UV-lightcuring , high strength
low viscous, capillary, for subsequent bonding
anaerobic/lightcuring
Viscosity/mPa⋅s:
12
Chem. Basis: Viscosity/mPa⋅s:
12
di-methacrylate-ester
Endfestigkeit: 10 hours
Handfestigkeit: 5 - 15 minutes (anaerobic), 20 - 40 seconds (light)
Group / Description
pipe sealing , low strength
high viscous, for all thread sizes
AM: pipe sealing , low strength
high viscous, for all thread sizes
anaerobic
Viscosity/mPa⋅s:
8000
Chem. Basis: Viscosity/mPa⋅s:
8000
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
pipe sealing , medium strength
high viscous, KTW-Reg. C 1078/00/st
AM: pipe sealing , medium strength
high viscous, KTW-Reg. C 1078/00/st
anaerobic
Viscosity/mPa⋅s:
5000 thix
Chem. Basis: Viscosity/mPa⋅s:
5000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
pipe sealing , medium strength
sealing of threaded and pipe connections on passive and inactive surfaces even without the use of an activator
AM: pipe sealing , medium strength
sealing of threaded and pipe connections on passive and inactive surfaces even without the use of an activator
anaerobic
Viscosity/mPa⋅s:
5.000 thix
Chem. Basis: Viscosity/mPa⋅s:
5.000 thix
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 6 minutes
Group / Description
pipe sealing , medium strength
high viscous
AM: pipe sealing , medium strength
high viscous
anaerobic
Viscosity/mPa⋅s:
8000
Chem. Basis: Viscosity/mPa⋅s:
8000
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
pipe sealing , medium strength
high viscous, liquid Teflon®, for all thread sizes, white
AM: pipe sealing , medium strength
high viscous, liquid Teflon®, for all thread sizes, white
anaerobic
Viscosity/mPa⋅s:
10 000 thix
Chem. Basis: Viscosity/mPa⋅s:
10 000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 10 minutes
Group / Description
pipe sealing , medium strength
high viscous, for all thread sizes, DVGW-certified
AM: pipe sealing , medium strength
high viscous, for all thread sizes, DVGW-certified
anaerobic
Viscosity/mPa⋅s:
500 000 thix
Chem. Basis: Viscosity/mPa⋅s:
500 000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 2 - 10 minutes
Group / Description
pipe sealing , high strength
flexible pipe sealing for metat/metal, metal/synthetics, synthetics/synthetics
AM: pipe sealing , high strength
flexible pipe sealing for metat/metal, metal/synthetics, synthetics/synthetics
anaerobic
Viscosity/mPa⋅s:
2000 thix
Chem. Basis: Viscosity/mPa⋅s:
2000 thix
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 3 - 10 minutes
Group / Description
pipe sealing , high strength
for securing and sealing of threaded and pipe connections with passive and inactive surfaces even without the use of an activator
AM: pipe sealing , high strength
for securing and sealing of threaded and pipe connections with passive and inactive surfaces even without the use of an activator
anaerobic
Viscosity/mPa⋅s:
5.000 thix
Chem. Basis: Viscosity/mPa⋅s:
5.000 thix
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 2 - 6 minutes
Group / Description
pipe sealing , high strength
pipe- and surface sealing, hard to disassemble, field of hydraulics, DVGW approved - up to 65 bar pressure
AM: pipe sealing , high strength
pipe- and surface sealing, hard to disassemble, field of hydraulics, DVGW approved - up to 65 bar pressure
anaerobic
Viscosity/mPa⋅s:
8000 thix
Chem. Basis: Viscosity/mPa⋅s:
8000 thix
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 3 - 10 minutes
Group / Description
pipe sealing
High viscosity product recommended especially for pipe threads exposed to heat
AM: pipe sealing
High viscosity product recommended especially for pipe threads exposed to heat
anaerobic
Viscosity/mPa⋅s:
4.000 thix
Chem. Basis: Viscosity/mPa⋅s:
4.000 thix
Di-Methacrylatester
Endfestigkeit: 24 Stunden
Handfestigkeit: 5 - 15 Minuten
Group / Description
surface sealing , low strength
pasty, run-resistant, for sealing of flanges, easy to detach
AM: surface sealing , low strength
pasty, run-resistant, for sealing of flanges, easy to detach
anaerobic
Viscosity/mPa⋅s:
70 000 pasty
Chem. Basis: Viscosity/mPa⋅s:
70 000 pasty
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 5 - 15 minutes
Group / Description
surface sealing , medium strength
pasty, run-resistant, for sealing of flanges, detachable
AM: surface sealing , medium strength
pasty, run-resistant, for sealing of flanges, detachable
anaerobic
Viscosity/mPa⋅s:
70 000 pasty
Chem. Basis: Viscosity/mPa⋅s:
70 000 pasty
di-methacrylate-ester
Endfestigkeit: 10 hours
Handfestigkeit: 2 - 15 minutes
Group / Description
surface sealing , medium strength
pasty, run-resistant, for sealing of pipe connections, detachable
AM: surface sealing , medium strength
pasty, run-resistant, for sealing of pipe connections, detachable
Viscosity/mPa⋅s:
70.000 mPas
dimethacrylate-ester
Endfestigkeit: 10 hours
Handfestigkeit: 2-15 minutes
Group / Description
joining , medium strength
for bonding of cylindrical fitting parts, medium strength, medium viscosity
AM: joining , medium strength
for bonding of cylindrical fitting parts, medium strength, medium viscosity
anaerobic
Viscosity/mPa⋅s:
700
Chem. Basis: Viscosity/mPa⋅s:
700
dimethacrylate-ester
Endfestigkeit: 24 hours
Handfestigkeit: 5-20 minutes
Group / Description
joining , high strength
extremely fast cure, highest strength, temperature resistant
AM: joining , high strength
extremely fast cure, highest strength, temperature resistant
anaerobic
Viscosity/mPa⋅s:
200
Chem. Basis: Viscosity/mPa⋅s:
200
di-methacrylate-ester
Endfestigkeit: 8 hours
Handfestigkeit: 1 - 7 minutes
Group / Description
joining , high strength
for fastening of bearings, extremely fast cure, super high strength, temperature resistant, not classified
AM: joining , high strength
for fastening of bearings, extremely fast cure, super high strength, temperature resistant, not classified
anaerobic
Viscosity/mPa⋅s:
200
Chem. Basis: Viscosity/mPa⋅s:
200
di-methacrylate-ester
Endfestigkeit: 12 hours
Handfestigkeit: 3 - 10 minutes
Group / Description
joining , high strength
fast cure even on passive surfaces
AM: joining , high strength
fast cure even on passive surfaces
anaerobic
Viscosity/mPa⋅s:
500
Chem. Basis: Viscosity/mPa⋅s:
500
di-methacrylate-ester
Endfestigkeit: 6 hours
Handfestigkeit: 1 - 7 minutes
Group / Description
joining , high strength
high viscous, extreme strength, DVGW-certified
AM: joining , high strength
high viscous, extreme strength, DVGW-certified
anaerobic
Viscosity/mPa⋅s:
3000
Chem. Basis: Viscosity/mPa⋅s:
3000
di-methacrylate-ester
Endfestigkeit: 6 hours
Handfestigkeit: 1 - 7 minutes
Group / Description
joining , high strength
for the repair of blowholes and cracks on worn-out bearings, bushings and hub- shaft connections
AM: joining , high strength
for the repair of blowholes and cracks on worn-out bearings, bushings and hub- shaft connections
anaerobic
Viscosity/mPa⋅s:
50.000 thix
Chem. Basis: Viscosity/mPa⋅s:
50.000 thix
di-methacrylate-ester
Endfestigkeit: 24 hours
Handfestigkeit: 3 - 10 minutes
Group / Description
anaerobic/UV-lightcuring , high strength
low viscous, anaerobic and light curing
AM: anaerobic/UV-lightcuring , high strength
low viscous, anaerobic and light curing
anaerobic/lightcuring
Viscosity/mPa⋅s:
500
Chem. Basis: Viscosity/mPa⋅s:
500
di-methacrylate-ester
Endfestigkeit: 3 hours
Handfestigkeit: 5 - 15 minutes (anaerobic), 20 - 40 seconds (light)
Group / Description
anaerobic/UV-lightcuring , high strength
high viscous, gap filling
AM: anaerobic/UV-lightcuring , high strength
high viscous, gap filling
anaerobic/lightcuring
Viscosity/mPa⋅s:
8000 thix
Chem. Basis: Viscosity/mPa⋅s:
8000 thix
di-methacrylate-ester
Endfestigkeit: 10 hours
Handfestigkeit: 5 - 15 min. (anaerobic), 20 - 40 sec. (light)