Article:
 MK 4422
Group / Description
joining , high strength

extremely fast cure, highest strength, temperature resistant
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4423
Group / Description
joining , high strength

for fastening of bearings, extremely fast cure, super high strength, temperature resistant, not classified
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
3 - 10 minutes
Article:
 MK 4425
Group / Description
joining , high strength

fast cure even on passive surfaces
AM:
anaerobic

Viscosity/mPa⋅s:
500
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
6 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4433
Group / Description
joining , high strength

high viscous, extreme strength, DVGW-certified
AM:
anaerobic

Viscosity/mPa⋅s:
3000
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
6 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4451
Group / Description
joining , high strength

or the repair of blowholes and cracks on worn-out bearings, bushings and hub- shaft connections
AM:
anaerobic

Viscosity/mPa⋅s:
50.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
24 hours
Handfestigkeit:
3 - 10 minutes